Bond,Seal Super x no.8008 135ml clear

  • Bond,Seal Super x no.8008 135ml clear
  • Bond,Seal Super x no.8008 135ml clear
Model No.︰AX-139,AX-123
Brand Name︰CEMEDINE
Country of Origin︰Japan
Unit Price︰US $ 17.5 / pc
Minimum Order︰1 pc
Share on:

 Total 122 Related Items 
Prev96979899100Next

Product Description

Elastic adhesive | Super X

Cemedine Super X is an innovative one-part, quick cure adhesive with three key features: "Pressure-sensitive adhesion", "Elastic adhesion" and "Solvent-free adhesion", which are the ideal properties of adhesives. It is used around the world.

Features

Multi-purpose adhesive for high-performance bonding of numerous materials.

Super X products allow for adhesion of various types of plastics, rubbers and ceramics over an extensive range, and also over different types of metals. These products provide excellent adhesion over a very extensive range of materials, eliminating the need for selecting a particular adhesive for each type of material, as in the case of conventional adhesives.

One-part solventless type providing quick curing at room temperature

Curing reaction is caused by moisture absorbed from the air. Pressure-sensitive range is reached in this curing process about 10 min after application. If adherends are put together during this time, they bind instantaneously as in the case of rubber contact adhesive, eliminating the need for temporary fixation. Easy-to-use, safe, and clean adhesive featuring one-part solventless capable of quick curing at room temperature is provided.

High durability

Super X as elastic adhesives does not peel off. Once materials are adhered, Super X provides durability in the range from low temperature (-60°C) to high temperature (120°C). Because of the rubber state of the hard film, the Super X sufficiently follows expansion, shrinkage and other changes of adherends.

Siloxane-free

There is not including low molecular weight cyclosiloxane. (D3 to D10 Cyclosiloxane compound)

Application

  • For bonding application that requires initial rise strength.
  • For bonding applications of dissimilar materials with different coefficients of thermal expansion.
  • For bonding applications that require durability, such as thermal cycling.
  • There are two ways to use: single sided and double sided. 
    Please use properly depending on the material and the conditions to be attached.

[Method 1: Single-sided application]

  • In the case of porous material.
  • In the case of the bonding area is small.

[Method 2: Double-sided application (like contact cement)]

  • In the case of non-porous materials such as metal, plastic and ceramic.
  • When the initial rising adhesion strength is required, such as warped parts, adhesion to vertical surfaces, adhesion of heavy materials, etc.

Initial curing process

s_t_elastic_superx_index_sx8008_katei960.jpg

Representative test data

Initial curing speed by environmental temperature

Tensile shear strength on each temperature

Tensile shear strength after heat aging

Tensile shear adhesive strength after High-temperature and High-humidity

Adhesive strength for various types of adherends

(MPa)

Adherends Tensile shear adhesive strength 
after 7-day curing
Metal Steel plate (SPCC, SPCD) 3.32 CF
Aluminum(*1) 4.26 CF
Stainless steel 2.24 AF
Copper 3.62 CF
Plastics Polycarbonate 3.29 CF
Bakelite 4.43 CF
ABS 3.10 CF
Unplasticized polyvinyl chloride 3.08 CF
Styrene 2.40 CF5 AF5
Acryl 3.22 CF
6-nylon 3.28 CF
FRP(*2) 2.92 CF
Polypropylene(*3) 2.77 CF5 AF5
PET(Polyethylene terephthalate) 2.22 CF3 AF7
PPS(Polyphenylene sulfide) 1.60 AF
PPO(Polyphenylene oxide) 3.16 CF
PAR(Polyarylate) 1.10 AF
Others Slate 1.01 MF
Plywood 3.60 CF

CF:Cohesion Failure, AF:Adhesive Failure, MF:Failure Modes

Coated on both sides, 50µm thick (one side),tension speed between adherends: 50mm/min

*1 and *2: Surface preparation causes adhesive strength to become uneven; it must be confirmed in advance. 
*3: Primer (Cemedine PP-7F) to be used.

Adhesive strength for various types of rubbers

(N/mm)

Adherends Peeling adhesive strength 
after 7-day curing
Rubbers NBR 0.27 AF
Silicone rubber 0.45 AF
EPDM 0.60 AF
EPDM(*) 2.73 CF
CR (Chloroprene rubber) (*) 0.43 AF

(*)…Degreasing by MEK after treatment by sandpaper (#120)

Chemicals resistance

(MPa)

Chemicals Tensile shear strength 
after dipping in chemicals
Initial Value 2.24 AF
Water 3.00 CF5 AF5
Acetic acid (1% water solution) 2.05 CF4 AF6
Acetic acid (10% water solution) 1.22 CF3 AF7
Sulfuric acid (3% water solution) 2.93 CF2 AF8
Sulfuric acid (30% water solution) 2.05 AF
Sodium hydroxide (1% water solution) 2.84 CF5 AF5
Sodium hydroxide (10% water solution) 3.29 CF2 AF8
Machine oil (Idemitsu: Mechanic Oil) 2.96 CF5 AF5
Salt (10% water solution) 3.16 CF4 AF6
MEK* 0.11 AF
n-Hexane* 0.56 AF

CF:Cohesion Failure, AF:Adhesive Failure  

Adherends : Stainless steel x Stainless steel  
Surface preparation : Degreasing with MEK 
Coating quantity : Coated on both sides 50μm thick (per side)  
Open time : 2 min  
Pressing : 2 pinches  
Curing : 23°C50%RH x 7 days  
Chemical immersion : 23°C x 7 days  
Tension speed : 50 mm/min  
Destruction State : Confirmation by seeing  
*… Deterioration of solvent is observed, but no problem with short-time contact, for example, in washing.

Property

  Super X No.8008
White Black L Black LL Black Clear
Type One component type Elastic Adhesive
Standard type Low viscosity type Clear type
Base Special polymer containing silyl group
Appearance White paste Black paste Light yellow clear paste
Viscosity Pa・s/23°C 85.0 85.0 22.0 19.0 82.6
Specific gravity g/cm3 1.27 1.27 1.25 1.22 1.07
Skin over time 23°C 11min 11min 11min 12min 8.5min
Adhesive property Tensile shear adhesive strength MPa 4.0 4.0 3.5 3.3 3.5
T type peeling adhesive strength N/mm 2.0 2.0 2.1 1.0 3.4
Curing properties Hardness Shore A 43 43 35 34 50
Glass transfer point °C -63 -63 -68 -59 -64
Breaking strength MPa 2.5 2.5 1.3 0.9 4.0
Elongation at break % 200 200 320 200 170
Electric Characteristics Volume resistivity Ω・cm 1.1 x 1012 4.7 x 1011 1.2 x 1012 1.0 x 1012 1.3 x 1012
Dielectric constant 100Hz 6.15 7.07 6.99 6.56 3.89
Dielectric loss tangent 100Hz 0.22 0.34 0.24 0.25 0.11
Grade RoHS
RoHS
RoHS
RoHS
RoHS 
Capacity 170g 170g 170g   135ml
333ml 333ml 333ml 333ml 333ml
           

Description of the markexplanation

Price Terms︰FOB HONGKONG, FOB SHENZHEN
Payment Terms︰TT
Product Image



Related Products
Cemedine Reactive Acrylic Adhesive Y611
Cemedine Reactive Acrylic Adhesive Y611
US $ 27.5
Cemedine Reactive Acrylic Adhesive Y600H
Cemedine Reactive Acrylic Adhesive Y600H
US $ 27.5
Cemedine Reactive Acrylic Adhesive Y610
Cemedine Reactive Acrylic Adhesive Y610
US $ 27.5
Cemedine Reactive Acrylic Adhesive Y600
Cemedine Reactive Acrylic Adhesive Y600
US $ 27.5

Powered by DIYTrade.com
HomeContact UsSitemap