Cemedine Reactive Acrylic Adhesive Y610

Cemedine Reactive Acrylic Adhesive Y610

Model No.︰Y600 Y610 Y600H

Brand Name︰CEMEDINE

Country of Origin︰Japan

Unit Price︰US $ 27.5 / pc

Minimum Order︰1 pc

Inquire Now

Product Description

 

Reactive Acrylic Adhesive

The two-part acrylic adhesive, whose curing properties do not change much even if the mixing ratio and mixing status vary, has user friendliness almost equal to that of one-part adhesive.

Features

  • Reactive acrylic adhesive has the robust strength of a structural adhesive.
  • Reactive acrylic adhesive is cured quickly.
  • Reactive acrylic adhesive contains no inflammable solvent.
  • Reactive acrylic adhesive does not have as bad an odor as a conventional acrylic adhesive.
  • Reactive acrylic adhesive causes almost no skin irritation. unlike epoxy adhesive.
  • The adhesive property of reactive acrylic adhesive is unchanged, even on a slightly oily surface.

 Application

  • Assembly of building members
  • Assembly of signboard
  • Assembly of furniture
  • Adhesion and assembly of automotive and vehicle parts
  • Assembly of magnets
  • Assembly of sports goods

Product details
・Multi-purpose type : Y600, Y600H, Y610, Y620
・High heat resistance type : Y611BLACK S, Y612BLACK
・Flexible type : Y618LD, Y618H, Y630D
・Conventional type (*Odorous) : Y650 

Product data

Adhesive strength by mixing ratio

Oil surface adhesion

Heat aging resistance

High temperature high humidity durability

Heat shock testing

Chemical resistance

Property

Multi-purpose type

  Y600 Y600H Y610 Y620
Agent A Agent B Agent A Agent B Agent A Agent B Agent A Agent B
Application / Properties / Features High speed curing High viscosity High strength Slow curing
Base Acrylic resin Acrylic resin Acrylic resin Acrylic resin
External appearance Light blue Blue White Gray White Gray Light yellow Blue
Viscosity mPa・s/23°C 4,000 4,000 30,000 30,000 5,500 5,500 8,000 8,000
Mixing ratio 1:1 1:1 1:1 1:1
Pot life *1 23°C 30 s 2 min 3 min 6 min
Set time *2 23°C 3 min 4 min 6 min 20 min
Adhesive property Tensile shear strength MPa 23.2 19.4 26.0 21.1
T-peel strength N/mm 5.0 3.6 3.7 4.2
Curing properties Hardness Shore A 68 65 72 66
Glass transfer point °C 83 78 90 79
Elastic modulus MPa 767 742 935 778
Breaking strength MPa 16.2 14.0 19.0 16.1
Elongation at break % 26 8 6 25
Capacity 600g set 50g set 50g set 600g set
  10kg 600g set 2kg
       
         

*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).

High heat resistance type

  Y611BLACK S Y612BLACK
Agent A Agent B Agent A Agent B
Application / Properties / Features Hight strength / High heat resistance
Base Acrylic resin Acrylic resin
External appearance Light yellow Black Light yellow Black
Viscosity Pa・s/23°C 3,000 3,000 15,000 15,000
Mixing ratio 1:1 1:1
Pot life *1 23°C 3 min 1 min
Set time *2 23°C 7 min 3 min
Adhesive property Tensile shear strength MPa 28.4 29.2
T-peel strength N/mm 4.2 4.3
Curing properties Hardness Shore D 84 86
Glass transfer point °C 123 127
Elastic modulus MPa 1558 1615
Breaking strength MPa 32.9 33.7
Elongation at break % 3.5 3.2
Capacity 600g set 600g set
10kg/BIB 10kg/BIB
     

*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).

Flexible type

  Y618LD Y618H Y630D
Agent A Agent B Agent A Agent B Agent A Agent B
Application / Properties / Features Flexible / Low distortion Hight strength / High heat resistance
Base Acrylic resin Acrylic resin Acrylic resin
External appearance Red Blue Light yellow Light green Light yellow Light green
Viscosity Pa・s/23°C 5,000 5,000 15,000 15,000 4,000 4,000
Mixing ratio 1:1 1:1 1:1
Pot life *1 23°C 2 min 2 min 30 s 1 min 30 s
Set time *2 23°C 7 min 10 min 4 min 30 s
Adhesive property Tensile shear strength MPa 14.2 15.7 25.3
T-peel strength N/mm 5.9 5 4.6
Curing properties Hardness Shore D 47 55 83
Glass transfer point °C 61   118
Elastic modulus MPa 451   2414
Breaking strength MPa 10.5 10.6 32.1
Elongation at break % 40 51 2
Capacity 600g set 190mL set 600g set
10kg/BIB    
       

 

*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).

Conventional type SGA Y650 (*Odorous)

  Y650
Agent A Agent B
Base Acrylic resin
External appearance Blue Red
Viscosity mPa・s/23°C 3,220 3,320
Mixing ratio 1:1
Pot life *1 23°C 2 min 30 s
Set time *2 23°C 4 min 30 s
Adhesive property Tensile shear strength MPa 23.8
T-peel strength N/mm 4.6
Curing properties Hardness Shore D 60
Glass transfer point °C 83
Elastic modulus MPa 740
Breaking strength MPa 16.1
Elongation at break % 25
Capacity 2.5kg

*1 : After mixing agents A and B, immediately use the mixture to bond the materials (the pot life is an estimate).
*2 : Set time = Time required for the materials to adhere so that they will not peel off even when a tensile shear load of 5 kg is applied (SPCC steel plates with a size of 25 mm×100 mm×1.6 mm bonded with a lap length of 12.5 mm).

Price Terms︰ fob Hongkong, fob Shenzhen

Payment Terms︰ TT

Product Image