Cemedine SX-PPK1000(EXP) 333ml

Cemedine SX-PPK1000(EXP) 333ml

Model No.︰SX-PPK1000

Brand Name︰cemedine

Country of Origin︰Japan

Unit Price︰US $ 55.5 / pc

Minimum Order︰20 pc

Inquire Now

Product Description

Cemedine SX-PPK1000(EXP) 333 ML/Cartridge

Features

  1. Designed for polypropylene (PP) materials
    Excellent adhesion to polypropylene resin, which is normally adhesive-resistant.
     
  2. One-part type
    Does not require primer application ,improving the work environment and increasing work efficiency.
     
  3. Adhesive for bonding different types of materials
    Excellent adhesion to polypropylene resin and various other materials. This is an elastic adhesive which can ease thermal stress caused by a difference in thermal expansion coefficient among different types of materials.
     
  4. Flexible Cured properties
    Designed for cured film properties that are excellent in flexibility and followings, and has excellent peel adhesion.

    Application

  5. For bonding polypropylene resin with different types of materials.
    (Not suited for bonding materials such as polyethylene, fluorine, and polyacetal)
  6. For bonding that requires durability (e.g. in relation to thermal cycles).
  7. For bonding that requires waterproof performance.
  8. For bonding related to PP automotive parts, and electrical components and parts.
  9. Comparison with conventional adhesives

      Surface treatment method SX-PPK1000(EXP) Conventional
    adhesive
    Tensile shear strength (MPa)
    PP×PP
    Untreated 1.4 0.3
    Treated with PP dedicated primer Unnecessary 2.8
    Treated with Corona discharge (Once) Unnecessary 0.7
    (2 Times) 1.3
    180°degree peel strength (N/25mm )
    PP×Canvas
    Untreated 75 3
    Treated with PP dedicated primer Unnecessary 50
    Treated with Corona discharge (Once) Unnecessary 10
    (2 Times) 30

    Tensile shear strength
    Curing : 23°C50%RH x 7 days
    Coating quantity : Coated on both sides 100μm thick (per side)
    Application area : 25mm x 25mm
    Tension speed: 50mm/min

    180°degree peel strength
    Curing : 23°C50%RH x 7 days
    Coating quantity: Coated on both sides 300μm thick (per side)
    Pressing : Rubber roller
    Tension speed : 200mm/min

    Product data

    Tensile shear adhesive strength of PP (homopolymer) and various adherends

    (MPa)

    PP (Homopolymer )
    ×The following adherends
    Tensile shear strength
    PP 1.4 CF5 AF5
    PP (TALC 10wt%) 1.6 CF
    PVC 1.3 CF9 AF1(PP)
    PC 1.4 CF9 AF1(PP)
    ABS 1.4 CF6 AF4(PP)
    PMMA 1.6 CF8 AF2(PP)
    PA6 1.3 CF8 AF2(PP)
    SPCC 1.5 CF1 AF9(SPCC)
    AL 1.6 CF
    PET 1.6 CF
    PBT 1.6 CF
    PPO 1.5 CF8 AF2(PP)
    PPS 1.1 CF3 AF7(PPS)
    POM 1.1 CF3 AF7(POM)
    PA MXD6 1.3 CF5 AF5(MXD6)
    PEEK 2.2 CF
    FRP 1.6 CF
    SUS304 2B 0.8 AF(SUS)

    CF:Cohesion Failure, AF:Adhesive Failure

    The numbers indicate their proportion to the adhesion area.
    Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

    Curing : 23°C50%RH x 7 days
    Coating quantity : Coated on both sides 100μm thick (per side)
    Application area : 25mm x 25mm
    Tension speed : 50mm/min
    Destruction State : Confirmation by seeing

    Tensile shear adhesive strength of PP talc (PP containing 10% talc) and various adherends

    (MPa)

    PP (TALC) 
    x The following adherends
    Initial state 80°C x 1week 80°C85%RH x 1week
    PP (TALC) 1.6 CF 2.1 CF8 AF2(PP) 1.9 CF
    ABS 1.6 CF 2.1 CF4 AF6(ABS) 1.9 CF
    PMMA 1.5 CF 2.2 CF9 AF1(PP) 1.8 CF
    PBT 1.7 CF8 AF2(PP) 2.2 CF 1.8 CF
    PPO 1.7 CF9 AF1(PP) 2.2 CF 2.0 CF
    PPS 1.1 CF2 AF8(PPS) 2.2 CF 2.0 CF
    POM 1.0 CF3 AF7(POM) 1.0 CF2 AF8(POM) 1.0 CF2 AF8(POM)
    PA MXD6 1.6 CF 2.2 CF3 AF7(RENY) 1.4 CF2 AF8(RENY)
    SUS304 2B 0.7 AF(SUS) 2.2 CF3 AF7(SUS) 1.7 CF3 AF7(SUS)
    Aluminum 1.7 CF8 AF2(PP) 2.2 CF 2.0 CF
    Copper 1.6 CF2 AF8(Cu) 2.0 CF 1.9 CF

    CF:Cohesion Failure, AF:Adhesive Failure

    The numbers indicate their proportion to the adhesion area.
    Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

    Curing : 23°C50%RH x 7 days
    Open time : 5 min (10 min for metal / PP)
    Coating quantity : Coated on both sides 100μm thick (per side)
    Tension speed : 50mm/min
    Destruction State : Confirmation by seeing
    Pressing : 2 pinches

    Peeling adhesion strength with various adherends

    (N/25mm)

    Adherends x Canvas
    180°degree peel strength
    Initial state
    (23°C50%RH x 1week)
    Initial state
    + 80°C x 1week
    Initial state 
    + 80°C85%RH x 1week
    PP 75.3 CF7 AF3 84.2 CF 132.0 CF9 AF1
    PP (TALC 10wt%) 93.1 CF3 AF7 129.8 CF5 AF5 129.2 CF
    PC (Glass fiber 30wt%) 88.3 CF 108.4 CF 132.4 CF
    ABS 85.3 CF 105.4 CF 118.0 CF
    PC/ABS 92.0 CF 111.5 CF 127.5 CF
    PMMA 90.9 CF 111.6 CF 124.1 CF
    PA MXD6 107.3 CF 113.3 CF 52.8 AF
    PBT 80.2 CF 116.0 CF 118.5 CF
    PPO 87.5 CF 118.4 CF 130.5 CF
    PPS 89.7 CF 108.7 CF 131.0 CF
    PEEK 94.1 CF 102.5 CF 110.8 CF
    POM 67.9 CF5 AF5 83.5 CF5 AF5 46.5 CF1 AF9
    SPCC-SD 73.8 CF1 AF9 111.0 CF 110.8 CF
    SUS304 2B 41.6 AF 120.7 CF6 AF4 129.1 CF

    Tension speed : 200mm/min
    Destruction State : Confirmation by seeing

    Thermal shock test

    Tensile shear adhesive strength (MPa)

      PP x ABS PP x AL
    Initial state 1.4 CF6 AF4(PP) 1.6 CF
    100 cycles 1.9 CF7 AF4(PP) 2.0 CF7 AF3(PP)
    250 cycles 1.9 CF1 AF9(PP) 2.2 CF6 AF4(PP)
    500 cycles 2.3 CF2 AF8(PP) 2.8 CF6 AF4(PP)
    750 cycles 2.2 CF2 AF8(PP) 2.2 CF5 AF5(PP)
    1000 cycles 1.8 CF1 AF9(PP) 2.7 CF4 AF6(PP)
    1500 cycles 1.8 CF2 AF8(PP) 2.5 CF4 AF6(PP)

    CF:Cohesion Failure, AF:Adhesive Failure

    The numbers indicate their proportion to the adhesion area.
    Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

    Curing : 23°C50%RH x 7 days
    Coating quantity : Coated on both sides 100μm thick (per side)
    Application area : 25mm x 25mm
    Tension speed : 50mm/min
    Destruction State : Confirmation by seeing

    Heat or cold aging test

    Tensile shear adhesive strength (MPa)

      -35°C
    (PP x AB)
    -35°C
    (PP x AL)
    100°C
    (AL x AL)
    120°C
    (AL x AL)
    Initial 1.4 CF6 AF4(PP) 1.6 CF 1.9 CF 1.9 CF
    1 week 2.2 CF8 AF2(PP) 2.2 CF7 AF3(PP) 3.7 CF 3.3 CF
    2 weeks 2.2 CF7 AF3(PP) 2.2 CF7 AF3(PP) 3.5 CF 3.9 CF
    4 weeks 2.3 CF7 AF3(PP) 2.1 CF6 AF4(PP) 3.4 CF 3.9 CF
    8 weeks 2.2 CF8 AF2(PP) 2.1 CF7 AF3(PP) 3.5 CF 3.9 CF

    CF:Cohesion Failure, AF:Adhesive Failure

    The numbers indicate their proportion to the adhesion area. Parentheses in the case of AF indicate adherends in which Adhesive Failure has occurred.

    Curing: 23°C50%RH x 7 days 
    Test conditions : After curing, leave under each temperature condition 
    Coating quantity : Coated on both sides 100μm thick (per side) 
    Application area : 25mm x 25mm 
    Tension speed : 50mm/min 
    Destruction State : Confirmation by seeing

    Property

      SX-PPK1000(EXP)
    Application / Properties / Features Designed for polypropylene (PP) materials
    Type One-part moisture-curing elastic adhesive
    Base Acrylic modified silicone
    Appearance Slightly yellowish-white paste
    Viscosity Pa・s/23°C 120
    Density g/cm3 1.23
    Skin over time 23°C 15 min
    Depth curing mm 1.63
    Tensile shear strength PP(Talc 10wt%) MPa 1.6
    180° degree peel strength PP(Talc 10wt%) x Canvas N/25mm 93.1
    Curing properties Hardness Shore A 15
    Breaking strength MPa 1.2
    Elongation at break % 875
    Capacity 333ml

 