Epoxy Resin AdhesiveTwo Component Epoxy Adhesives

Features

  1. Reactive adhesive
  2. Solventless
  3. No gas produced during curing process
  4. Excellent adhesive strength
  5. Excellent heat and chemical resistance
  6. Small shrinkage by curing
  7. Small creep under load
  8. Excellent durability
  9. Superb insulation

    Application

    Applicable to Adherendss over an extensive range including metals and plastics

  10. Adhesion of cars, vehicles, vessels and aircraft
  11. Adhesion and sealing of electric equipment and electronic parts
  12. Adhesion of composite members used for construction work
  13. Assembly of precision equipment and artworks
  14. Adhesion of sporting equipment
  15. Product data

    Adhesive strength for various types of materials

    (Tensile shear adhesive strength: MPa)

    Adherends 1500 EP007 EP330
    Steel plate 15.5 14.8 7.8
    Aluminum 6.0 13.0 10.2
    Stainless steel - 22.0 16.3
    Copper 7.8 10.0 19.8
    Hard polyvinyl chloride 3.5 4.1* -
    Polystyrene 1.9 1.9 0.9
    Acryl 2.9 1.0 0.9
    FRP 12.3 8.0 3.9
    Melamine decorative board 5.4 - 43.1
    Lawan plywood 10.4* 10.0* 47.1*

    Chemical resistance test

    (Tensile shear adhesive strength: MPa)

    Chemicals 1500 EP007
    Initial value 15.5 14.8
    Aceton 12.5 17.6
    Toluene 12.5 17.3
    Trichloroethylene 12.8 17.4
    Methanol 12.0 17.4
    Gasoline 13.6 19.4
    Engine oil 11.2 21.5
    10% sulfuric acid 10.5 19.3
    10% NaOH 13.6 20.4
    Tap water 13.1 21.5

    Property

    Standard type

      1500 Super
    Base resin Hardener Base resin Hardener
    Application / Properties / Features General purpose use
    Type Two-part epoxy adhesive curing at room temperature
    Base Epoxy resin Polyamide Epoxy resin Polyamide
    Appearance Light yellow transparent Light brown transparent Light yellow translucent Light brown transparent
    Viscosity Pa・s/23°C 20 55 100 50
    Density g/cm3 1.16 0.97 1.14 0.99
    Mixing ratio 1 : 1 1 : 1
    Standard curing conditions 23°C×24hours 23°C×24hours
    Pot life Within 1 hour Within 1 hour
    Time required for effective curing 6hours 6hours
    Adhesive property Tensile shear strength MPa 15.7 15.1
    T-peel strength N/mm 0.4  
    Curing properties Hardness Shore D 82  
    Glass transfer point °C 54  
    Coefficient of water absorption % 0.8  
    Coefficient of linear expansion 7.1×10-5  
    Electric Characteristics Volume resistivity Ω・cm 7.1×1015  
    Capacity 500g 500g 15g set
    1kg 1kg 40g set
    3kg 3kg 110gset
    15kg 15kg    
           

    Fast curing type

      High-super 5 High-quick EP330/High-super 30 EP331
    Base resin Hardener Base resin Hardener Base resin Hardener Base resin Hardener
    Application / Properties / Features 5 minute epoxy 5 minute epoxy (antisagging type) 30 minute epoxy 30 minute epoxy (low-viscosity)
    Type Two-part epoxy adhesive curing at room temperature
    Base Epoxy resin Polyamide Epoxy resin Polyamide Epoxy resin Polyamide Epoxy resin Polyamide
    Appearance Blue translucent Light yellow translucent White Gray Pink translucent Light yellow translucent Light yellow translucent Light yellow translucent
    Viscosity Pa・s/23°C 125 65 600 400 70 160 4 7
    Density g/cm3 1.17 1.15 1.57 1.50 1.17 1.14 1.16 1.16
    Mixing ratio 1 : 1 1 : 1 1 : 1 1 : 1
    Standard curing conditions 23°C×24hours 23°C×24hours 23°C×24hours 23°C×24hours
    Pot life Within 5 minutes Within 5 minutes Within 30 minutes Within 30 minutes
    Time required for effective curing About 1 hour About 1 hour About 1 hour About 1 hour
    Adhesive property Tensile shear strength MPa 18.0 17.7 17.5 17.6
    T-peel strength N/mm 0.31 0.40 0.47  
    Curing properties Hardness Shore D 77   82 71
    Glass transfer point °C 47   43 41
    Coefficientof water absorption % 2.5   2.3 0.8
    Coefficient of linear expansion 10.7×10-5   6.7×10-5 7.1×10-5
    Electric Characteristics Volume resistivity Ω・cm 4.9×1013   3.8×1011 2.4×1015
    Capacity 6g set 50g set 6g set 1kg 1kg
    15g set 500g set 15g set    
    25g set   80g set    
    80g set     320mL set    
            3kg 3kg    
                 

    Transparent type

      1565 1565+Hardener D Excel-EPO
    Base resin Hardener 1565 Base resin Hardener D Base resin Hardener
    Application / Properties / Features 30 minute epoxy (transparent) High Transparent 10 minute epoxy (transparent)
    Type Two-part epoxy adhesive curing at room temperature Two-part thermosetting epoxy resin Two-part epoxy adhesive curing at room temperature
    Base Epoxy resin Polythiol Epoxy resin Polyamide Epoxy resin Polythiol
    Appearance Light yellow transparent Red browntransparent Light yellow transparent Light yellow transparent Colorless transparent Colorless transparent
    Viscosity Pa・s/23°C 1.5 1.5 1.5 0.001 20 20
    Density g/cm3 1.15 1.24 1.15 0.83 1.14 1.13
    Mixing ratio 1 : 1 100 : 15 1 : 1
    Pot life 23°C 30 min Within 3 hours Within 10 min
    Time required for effective curing 23°C 9 hours Heat curing 1 hour
    Standard curing conditions   60°C×2 hours  
    Cured properties Hardness Shore D 72   78
    Glass transfer point °C     46
    Coefficient of water absorption %     2.3
    Refractive index     1.55  
    Coefficient of linear expansion ppm/K     8.3×10-5
    Electric Characteristics Volume resistivity Ω・cm     6.2×1013
    Capacity 500g 500g 500g 500g 15g set
    1kg 1kg 1kg 1kg    
             

    Flexible type

      EP007 EP008
    Base resin Hardener Base resin Hardener
    Application / Properties / Features Flexible type Flexible type
    (antisagging)
    Type Two-part epoxy adhesive curing at room temperature
    Base Epoxy resin Modified polyamide resin Epoxy resin Modified polyamide resin
    Appearance Light yellow transparent Light brown transparent White translucent Light brown transparent
    Non volatiles wt% 99.7 99.0 99.0 99.0
    Viscosity Pa・s/23°C 12 34 275 100
    Density g/cm3 1.17 0.95 1.17 0.97
    Standard curing conditions 23°C×7 days 23°C×7 days
    80°C×1 hour 80°C×1 hour
    Mixing ratio 1 : 1 1 : 1
    Pot life 23°C 60 min. 60 min.
    Time required for effective curing 23°C 12 hours 12 hours
    Tensile shear strength MPa 22.0 23.0
    T-peel strength N/mm 2.2 1.8
    Cured properties Hardness Shore D 78 74
    Glass transfer point °C 56 50
    Elastic modulus MPa 129  
    Coefficient of water absorption % 0.7 1.8
    Coefficient of linear expansion   9.7×10-5 12×10-5
    Electric Characteristics Volume resistivity Ω・cm 4.0×1015 1.50×1015
    Surface resistivity Ω/sq 1.2×1016 2.95×1016
    Dielectric constant 1kHz 3.28 5.31
    Dielectric loss tangent 1kHz 1.32×10-2 7.96×10-2
    Capacity 500g 500g 320ml set
    15kg 15kg 500g 500g
        15kg 15kg